Dyneon fe 5840 q
0 likes248 views
Dyneon fluoroelastomers present no known health hazards when recommended handling precautions are followed. Potential hazards can exist during high temperature processing. FE 5840Q is a terpolymer that can be compounded using standard methods and offers properties suitable for O-rings and gaskets in automotive fuel systems, including clean running and excellent mold release. FE 5840Q has a fluorine content of 70.1%, specific gravity of 1.89, and Mooney viscosity of approximately 37.
![Safety/Toxicology
When recommended handling precautions are
followed, Dyneon fluoroelastomers present no
known health hazards. General handling precau-
tions include: (1) Store and use all Dyneon fluo-
roelastomers only in well ventilated areas. (2) Do
not smoke in areas contaminated with dust from
Dyneon fluoroelastomers. (3) Avoid eye contact.
(4) After handling Dyneon fluoroelastomers
wash any contacted skin with soap and water.
Potential hazards, including evolution of toxic
vapors, do exist during compounding or process-
ing under high temperature conditions. Before
processing Dyneon fluoroelastomers, consult
the product MSDS (Material Safety Data Sheet)
and follow all label directions and handling pre-
cautions. You should also read and follow all
directions from other compound ingredient sup-
pliers. Material Safety Data Sheets on Dyneon
products are available from your Dyneon Sales
Representative or by dialing 651-733-5353.
Recommended Processing
Procedures
Dyneon FE 5840Q can be compounded using
standard water cooled internal mixers or two-roll
mills with standard fillers and ingredients utilized
in typical fluoroelastomer formulations. The
dry ingredients should be blended before
adding to the masticated gum. For best results,
FE 5840Q should be banded on the mill several
minutes prior to adding the blended dry ingredi-
ents. Once mixed, the compounded stocks dis-
play excellent processing characteristics and
storage stability.
Product Form
FE 5840Q is packaged in slab form and is avail-
able in a returnable bulk shipping container sys-
tem for 1,320 lbs (600 kg) of material. The bulk
container system is comprised of 48 individual
green polyethylene bags containing 27.5 lbs
(12.5 kg) of product. Smaller quantities are avail-
able in 55.1 lb (25.0 kg) boxes.
Typical Properties (Data not for specification purposes)
Fluorine Content [QCM 50.18.3.C] 70.1%
Specific Gravity [QCM 14.10] 1.89
Color Opaque Off-White
Solubility Ketones and Esters
Mooney Viscosity Approx. 37
ML 1 + 10 @ 121属C (250属F) [QCM 2.14.4.C]
Features and
Benefits
Composition:
Ter-polymer of vinyli-
dene fluoride, hexa-
fluoropropylene and
tetrafluoroethylene
Recommended
alternative for Dyneon
FX 9038
Process targets:
compression,
injection and transfer
molding
Proprietary incorporat-
ed cure technology
High fluorine material
designed for O-ring
and gasket applica-
tions
Recommended for
automotive fuel
system applications
Clean running
Excellent mold
release
Dyneon
Fluoroelastomer
FE 5840Q
Technical Information
98-0504-1189-5.qxd 1/4/01 11:17 AM Page 1](https://image.slidesharecdn.com/dyneonfe5840q-130501124630-phpapp01/85/Dyneon-fe-5840-q-1-320.jpg)
![ISO 9001/QS-9000
All Dyneon
fluoroelastomers are manufactured at ISO 9001 registered facilities.
Dyneon
fluoroelastomers produced in North America are manufactured at
QS-9000 registered facilities.
Typical Properties of Vulcanizate
(Data not for specification purposes)
Compound phr
FE 5840Q 100
MT Black (N990) 30
MgO 3
Ca(OH)2 6
Typical Rheological Properties
Monsanto Moving Die Rheometer (MDR2000速
)
100 cpm, 0.5属 Arc, 6 minutes [QCM 2.19.1.C]
Temperature 属C (属F) 177属 (350属) 200属 (392属)
ML, Minimum Torque, inch-lb (dN m) 1.7 (1.9) 1.7 (1.9)
ts2, Time to 2 inch-lb rise from minimum - 1.3 0.4
minutes
t50, Time to 50% cure - minutes 1.6 0.5
t90, Time to 90% cure - minutes 2.0 0.6
MH, Maximum Torque, inch-lb (dN m) 25.5 (28.8) 24.0 (27.1)
Typical Physical Properties [QCM 125.3.C and 125.17.C]
Press Cure 5 minutes @ 177属C (350属F)
Post Cure 24 hours @ 260属C (500属F)
Tensile, psi (Mpa) 2000 (13.8)
100% Modulus, psi (Mpa) 980 (6.8)
Elongation at break, % 210
Hardness, Shore A (ASTM D 2240) 84
Compression Set, %, [ASTM D 395 Method B (O-rings)]
Aged 70 hours @ 200属C (392属F) 26
TR10 [ASTM D 1329] 属C (属F) -7 (19)
Technical Information and Test Data
Technical information, test data, and advice provided by Dyneon personnel are based
on information and tests we believe are reliable and are intended for persons with
knowledge and technical skills sufficient to analyze test types and conditions, and to
handle and use raw polymers and related compounding ingredients. No license
under any Dyneon or third party intellectual rights is granted or implied by virtue of
this information.
Product Identification
The Q product designation indicates that this is a newly commercialized product
and Dyneon reserves the right to make additional process modifications without
notice to purchasers as long as the product meets Dyneon published specifications.
Once the commercial production process for this product is optimized and fixed,
the Q designation will be dropped from the product code.
FE 5840Q
Dyneon is a trademark of Dyneon
MDR2000 is a trademark of Monsanto
Important Notice:
Because conditions of product use are
outside Dyneons control and vary widely,
user must evaluate and determine whether
a Dyneon product will be suitable for users
intended application before using it.
The following is made in lieu of all
express and implied warranties
(including warranties of merchantabili-
ty and fitness for a particular purpose):
If a Dyneon product is proved to be
defective, Dyneons only obligation,
and users only remedy, will be, at
Dyneons option, to replace the quantity
of product shown to be defective
when user received it or to refund
users purchase price. In no event will
Dyneon be liable for any direct, indirect,
special, incidental, or consequential
loss or damage, regardless of legal
theory, such as breach of warranty or
contract, negligence, or strict liability.
息 Dyneon 2000
Issued:12/00
Printed in USA
98-0504-1189-5
All Rights Reserved
Dyneon LLC
6744 33rd Street North
Oakdale, MN 55128
Phone:+1 800 723 9127
+1 651 733 5353
Fax:+1 651 737 7686
www.dyneon.com
98-0504-1189-5.qxd 1/4/01 11:17 AM Page 2](https://image.slidesharecdn.com/dyneonfe5840q-130501124630-phpapp01/85/Dyneon-fe-5840-q-2-320.jpg)
Dyneon fe 5840 q
- 1. Safety/Toxicology When recommended handling precautions are followed, Dyneon fluoroelastomers present no known health hazards. General handling precau- tions include: (1) Store and use all Dyneon fluo- roelastomers only in well ventilated areas. (2) Do not smoke in areas contaminated with dust from Dyneon fluoroelastomers. (3) Avoid eye contact. (4) After handling Dyneon fluoroelastomers wash any contacted skin with soap and water. Potential hazards, including evolution of toxic vapors, do exist during compounding or process- ing under high temperature conditions. Before processing Dyneon fluoroelastomers, consult the product MSDS (Material Safety Data Sheet) and follow all label directions and handling pre- cautions. You should also read and follow all directions from other compound ingredient sup- pliers. Material Safety Data Sheets on Dyneon products are available from your Dyneon Sales Representative or by dialing 651-733-5353. Recommended Processing Procedures Dyneon FE 5840Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formulations. The dry ingredients should be blended before adding to the masticated gum. For best results, FE 5840Q should be banded on the mill several minutes prior to adding the blended dry ingredi- ents. Once mixed, the compounded stocks dis- play excellent processing characteristics and storage stability. Product Form FE 5840Q is packaged in slab form and is avail- able in a returnable bulk shipping container sys- tem for 1,320 lbs (600 kg) of material. The bulk container system is comprised of 48 individual green polyethylene bags containing 27.5 lbs (12.5 kg) of product. Smaller quantities are avail- able in 55.1 lb (25.0 kg) boxes. Typical Properties (Data not for specification purposes) Fluorine Content [QCM 50.18.3.C] 70.1% Specific Gravity [QCM 14.10] 1.89 Color Opaque Off-White Solubility Ketones and Esters Mooney Viscosity Approx. 37 ML 1 + 10 @ 121属C (250属F) [QCM 2.14.4.C] Features and Benefits Composition: Ter-polymer of vinyli- dene fluoride, hexa- fluoropropylene and tetrafluoroethylene Recommended alternative for Dyneon FX 9038 Process targets: compression, injection and transfer molding Proprietary incorporat- ed cure technology High fluorine material designed for O-ring and gasket applica- tions Recommended for automotive fuel system applications Clean running Excellent mold release Dyneon Fluoroelastomer FE 5840Q Technical Information 98-0504-1189-5.qxd 1/4/01 11:17 AM Page 1
- 2. ISO 9001/QS-9000 All Dyneon fluoroelastomers are manufactured at ISO 9001 registered facilities. Dyneon fluoroelastomers produced in North America are manufactured at QS-9000 registered facilities. Typical Properties of Vulcanizate (Data not for specification purposes) Compound phr FE 5840Q 100 MT Black (N990) 30 MgO 3 Ca(OH)2 6 Typical Rheological Properties Monsanto Moving Die Rheometer (MDR2000速 ) 100 cpm, 0.5属 Arc, 6 minutes [QCM 2.19.1.C] Temperature 属C (属F) 177属 (350属) 200属 (392属) ML, Minimum Torque, inch-lb (dN m) 1.7 (1.9) 1.7 (1.9) ts2, Time to 2 inch-lb rise from minimum - 1.3 0.4 minutes t50, Time to 50% cure - minutes 1.6 0.5 t90, Time to 90% cure - minutes 2.0 0.6 MH, Maximum Torque, inch-lb (dN m) 25.5 (28.8) 24.0 (27.1) Typical Physical Properties [QCM 125.3.C and 125.17.C] Press Cure 5 minutes @ 177属C (350属F) Post Cure 24 hours @ 260属C (500属F) Tensile, psi (Mpa) 2000 (13.8) 100% Modulus, psi (Mpa) 980 (6.8) Elongation at break, % 210 Hardness, Shore A (ASTM D 2240) 84 Compression Set, %, [ASTM D 395 Method B (O-rings)] Aged 70 hours @ 200属C (392属F) 26 TR10 [ASTM D 1329] 属C (属F) -7 (19) Technical Information and Test Data Technical information, test data, and advice provided by Dyneon personnel are based on information and tests we believe are reliable and are intended for persons with knowledge and technical skills sufficient to analyze test types and conditions, and to handle and use raw polymers and related compounding ingredients. No license under any Dyneon or third party intellectual rights is granted or implied by virtue of this information. Product Identification The Q product designation indicates that this is a newly commercialized product and Dyneon reserves the right to make additional process modifications without notice to purchasers as long as the product meets Dyneon published specifications. Once the commercial production process for this product is optimized and fixed, the Q designation will be dropped from the product code. FE 5840Q Dyneon is a trademark of Dyneon MDR2000 is a trademark of Monsanto Important Notice: Because conditions of product use are outside Dyneons control and vary widely, user must evaluate and determine whether a Dyneon product will be suitable for users intended application before using it. The following is made in lieu of all express and implied warranties (including warranties of merchantabili- ty and fitness for a particular purpose): If a Dyneon product is proved to be defective, Dyneons only obligation, and users only remedy, will be, at Dyneons option, to replace the quantity of product shown to be defective when user received it or to refund users purchase price. In no event will Dyneon be liable for any direct, indirect, special, incidental, or consequential loss or damage, regardless of legal theory, such as breach of warranty or contract, negligence, or strict liability. 息 Dyneon 2000 Issued:12/00 Printed in USA 98-0504-1189-5 All Rights Reserved Dyneon LLC 6744 33rd Street North Oakdale, MN 55128 Phone:+1 800 723 9127 +1 651 733 5353 Fax:+1 651 737 7686 www.dyneon.com 98-0504-1189-5.qxd 1/4/01 11:17 AM Page 2