Internal meeting developed at Institut des Mat└riaux Jean Rouxel (Nantes, France) during January 2014, regarding nickel oxide deposited under different parameters.

1 of 5
NiO results (third part) Javier Garc┴a Molleja In collaboration with: Julien Keraudy Pierre-Yves Jouan
NiO9: peak broadening T (nm) Peak Gauss Lorentz 100 111 2.48789E-8 0.57667 300 111 2.98835E-6 0.33632 500 111 8.70928E-6 0.42600 1000 111 0.26845 0.18839 Bias Peak Gauss Lorentz 0 111 0.26900 0.16691 50 111 0.22908 0.12828 100 111 0.21691 0.12883 200 111 0.23563 0.14752 300 111 0.34154 0.10787 400 111 0.20434 0.22687 500 111 2.6613E-6 0.44118
NiO9 with thickness 0 500 1000 1500 2000 2500 0.0 0.5 1.0 Contribution Thickness 220Cont 200Cont 111Cont
NiO9 with bias 0 100 200 300 400 500 0.0 0.2 0.4 0.6 0.8 1.0 Contribution Bias 220Cont 200Cont 111Cont
Stress by thickness

More Related Content

Results in NiO (3 of 3)

  • 1. NiO results (third part) Javier Garc┴a Molleja In collaboration with: Julien Keraudy Pierre-Yves Jouan
  • 2. NiO9: peak broadening T (nm) Peak Gauss Lorentz 100 111 2.48789E-8 0.57667 300 111 2.98835E-6 0.33632 500 111 8.70928E-6 0.42600 1000 111 0.26845 0.18839 Bias Peak Gauss Lorentz 0 111 0.26900 0.16691 50 111 0.22908 0.12828 100 111 0.21691 0.12883 200 111 0.23563 0.14752 300 111 0.34154 0.10787 400 111 0.20434 0.22687 500 111 2.6613E-6 0.44118
  • 3. NiO9 with thickness 0 500 1000 1500 2000 2500 0.0 0.5 1.0 Contribution Thickness 220Cont 200Cont 111Cont
  • 4. NiO9 with bias 0 100 200 300 400 500 0.0 0.2 0.4 0.6 0.8 1.0 Contribution Bias 220Cont 200Cont 111Cont